Conformable and die-cuttable biaxially oriented films and labelstocks

ABSTRACT

This invention relates to die-cuttable stretch oriented films wherein the tensile modulus of the film in the machine direction is greater than the tensile modulus in the cross direction and the tensile modulus in the cross direction is about 150,000 psi or less. The oriented films are useful in particular for preparing adhesive containing labelstock for use in adhesive labels.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a division of copending U.S. application Ser. No. 10/236,769 filed on Sep. 6, 2002 which is a division of copending U.S. application Ser. No. 09/531,978 filed on Mar. 20, 2002.

FIELD OF THE INVENTION

This invention relates to conformable and die-cuttable biaxially oriented films, and more particularly to biaxially stretch-oriented monolayer and multilayer films.

BACKGROUND OF THE INVENTION

It has long been known to manufacture and distribute pressure-sensitive adhesive stock for labels by providing a layer of face or facestock material for the label or sign backed by a layer of pressure-sensitive adhesive which in turn is covered by a release liner or carrier. The liner or carrier protects the adhesive during shipment and storage and allows for efficient handling of an array of individual labels after the labels are die-cut and the matrix is stripped from the layer of facestock material and up to the point where the individual labels are dispensed in sequence on a labeling line. During the time from die-cutting to dispensing, the liner or carrier remains uncut and may be rolled and unrolled for storage, transit and deployment of the array of individual labels carried thereon.

Failure to reliably dispense is typically characterized by the label following the carrier around a peel plate without dispensing or “standing-off” from the carrier for application to the substrate. Such failure to dispense is believed to be associated with excessive release values between the label facestock material and the liner. Dispensability also is dependent upon the stiffness of the facestock. Failure to dispense may also be characterized by the wrinkling of the label due to lack of label stiffness at the dispensing speed as it is transferred from the carrier to the substrate. Another particular need in many labeling applications is the ability to apply polymeric-film labels at high line speeds, since an increase in line speed has obvious cost saving advantages.

In many label applications, it is desirable that the facestock material be a film of polymeric material which can provide properties lacking in paper, such as clarity, durability, strength, water-resistance, abrasion-resistance, gloss and other properties. Historically, polymeric facestock material of thicknesses greater than about 3 mils (75 microns) have been used in order to assure dispensability in automatic labeling apparatuses. For example, plasticized polyvinyl chloride films about 3.5 to 4.0 mils (87.5 to 100 microns) thick were used in label application because these films exhibited the desired flexibility characteristics. However, the migration of the plasticizers used in PVC films to convert the normally rigid films to flexible films was recognized as a major problem area for these types of films resulting in loss of desirable properties such as adhesion, color buildup, shrinkage, and flexibility. Eventually, migration of the plasticizer results in wrinkling, cracking and visual deterioration of the facestock and/or label. Also, it is desirable to reduce the thickness or “down-gauge” the facestock material in order to attain savings in material costs. Such reduction in facestock thickness often has resulted in reduced stiffness and the inability to die-cut and dispense the labels in a reliable commercially acceptable manner using automatic machinery. There also was pressure for environmental reasons to prepare labels from polymer facestocks other than polyvinyl chloride.

Polymeric materials suggested in the prior art as useful in preparing labels include biaxially-oriented polypropylene (“BOPP”) of thicknesses down to about 2.0 mils (50 microns). These materials provide cost savings as they are relatively inexpensive, and they have sufficient stiffness to dispense well. However, these materials also have relatively high tensile modulus values in both machine-direction (MD) and cross direction (CD) which results in labels which are not very conformable.

Related conformability problems have been encountered in respect to rigid surfaces such as glass. For example, when biaxially-oriented films are applied to rigid substrates such as glass bottles, the application is not completely successful. The relatively stiff labels have a tendency to bridge surface depressions and the mold seams resulting from bottle-forming processes resulting in an undesirable surface appearance of the applied label simulating trapped air bubbles. This has somewhat impeded the use of pressure-sensitive adhesive labels to replace priorglass bottle labeling techniques such as ceramic ink directly bonded to the bottle surface during glass bottle manufacturing processes as customers find the appearance unattractive. Such ceramic ink techniques are environmentally undesirable due to objectionable ink components and the contamination of the ink in the crushed bottle glass in recycling processes. Attempts to use the relatively stiff oriented polypropylene films on flexible substrates such as plastic bottles also have not been completely successful because the labels do not have the flexibility required to conform to the flexible plastic containers. Oriented polypropylene films are also more difficult to print than PVC or polyethylene films.

Other useful materials are unoriented polyethylene and polypropylene films that are also relatively inexpensive and conformable. However, both of these films are difficult to die-cut and do not dispense well at low calipers. In Europe, an unoriented, relatively thick polyethylene facestock has been used successfully in preparing labels. The facestock is die-cuttable and the labels can be dispensed in high speed automatic dispensing equipment. The normal thickness of this “standard” polyethylene facestock in Europe is about 4.0 mils (100 microns). Attempts to reduce the gauge of the polyethylene facestock to reduce costs has not yet met with any degree of success because the thinner polyethylene facestock is not readily die-cuttable with the die leaving a mark on the liner and stringers on the cut label. Additionally, the thinner facestock becomes difficult to dispense at higher speeds over a peel plate because of reduced stiffness.

SUMMARY OF THE INVENTION

One embodiment of this invention is a die-cuttable, biaxially stretch-oriented monolayer film comprising a polyethylene having a density of about 0.940 g/cm³ or less, a propylene polymer or copolymer, or mixtures thereof, wherein the tensile modulus of the film in the machine direction is greater than the tensile modulus in the cross direction, the tensile modulus of the film in the cross direction is about 150,000 psi or less, and the film is free of copolymers of ethylene with an ethylenically unsaturated carboxylic acid or ester. In one embodiment, the biaxially oriented monolayer films have been biaxially stretch-oriented and heat set.

In another embodiment, the invention relates to a die-cuttable, stretch-oriented multilayer film comprising

-   -   (A) a base layer having an upper surface and a lower surface,         and comprising polyethylene having a density of about 0.940         g/cm³ or less, a propylene homopolymer or copolymer, or mixtures         thereof wherein the base layer is free of copolymers of ethylene         with an ethylenically unsaturated carboxylic acid or ester, and     -   (B) a first skin layer of a thermoplastic polymer bonded to the         upper surface of the base layer, wherein the tensile modulus of         the multilayer film in the machine direction is greater than the         tensile modulus in the cross direction, and the tensile modulus         in the cross direction is about 150,000 psi or less. The         biaxially oriented multilayer films are useful in particular in         preparing adhesive containing labelstock for use in adhesive         labels.

In yet another embodiment, the invention relates to a die-cuttable, biaxially stretch-oriented monolayer film comprising at least one polyolefin wherein the film has been stretch-oriented in the machine direction at a stretch ratio of about 9:1 to about 10:1, and in the cross direction at a stretch ratio of from greater than 1:1 to about 3:1.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention, in one embodiment, relates to the discovery that biaxially stretch-oriented monolayer and multilayer films can be prepared which are characterized as having improved conformability, die-cuttability, and/or dispensability. In some embodiments, films having improved clarity can be prepared. Although conformable films usually have poor die-cutting properties, the present invention provides conformable films that have acceptable die-cutting properties, and, therefore, these films may be used for labeling bottles and tubes or in other label applications that require clarity and conformability. Multilayered film constructions can be prepared in accordance with the present invention having skin layers designed to provide printability, or to provide other desirable characteristics such as stiffness so that the film can be down gauged, or both.

In one embodiment, the biaxially stretch-oriented monolayer films of the present invention comprise a polyethylene having a density of about 0.940 g/cm³ or less, a propylene polymer or copolymer, or mixtures thereof, wherein the tensile modulus of the film in the machine direction is greater than the tensile modulus in the cross direction, the tensile modulus of the film in the cross direction is about 150,000 psi or less, and the film is free of copolymers of ethylene with an ethylenically unsaturated carboxylic acid or ester.

Useful ethylene homopolymers include those having densities of about 0.940 or less. Polyethylenes having densities of from 0.850 to about 0.925 g/cm³ generally are referred to as low density polyethylenes, and polyethylenes having densities between about 0.925 and 0.940 g/cm³ are referred to in the art as being medium density polyethylenes. The low and medium density polyethylenes also may be characterized as having a melt index (as determined by ASTM Test D1238, condition E) in the range of from 0.5 to about 25. In addition to the above densities, and melt indices, the low density polyethylenes may be characterized by tensile strengths of between about 2200 to about 3200 psi (typically about 2700 psi), and the medium density polyethylenes may be characterized as having tensile strengths of between about 3000 and about 4000 psi (typically about 3400 psi).

Low and medium density polyethylene useful in the first skin layer of the facestock of this invention are available commercially from a variety of sources. Examples of useful polyethylenes are summarized in the following Table I. TABLE I Commercial Polyethylenes Commercial Melt Index Designation Company (g/10 mins) Density (g/cm³) Rexene 1017 Rexene 2.0 0.920 Rexene 1058 Rexene 5.5 0.922 Rexene 1080 Rexene 2.0 0.930 Rexene 2030 Rexene 5.0 0.919 Rexene 2034 Rexene 7.5 0.925 Rexene 2038 Rexene 9.0 0.917 Rexene 2040 Rexene 12.0 0.917 Rexene 2049 Rexene 20.0 0.917 NA-334 Equistar 6.0 0.918 NA-217 Equistar 5.5 0.923 NA 285-003 Equistar 6.2 0.930 Exact 3027 Exxon 3.5 0.900 Exact 3022 Exxon 9.0 0.905 Exact 3139 Exxon 7.5 0.900 SLP 9053 Exxon 7.5 0.900 Affinity PF1140 Dow Chemical 1.6 0.895 Sclair 11G1 Nova 0.72 0.920 Dowlex 2027 Dow Chemical 4.0 0.941

The monolayer film may comprise a propylene homopolymer or copolymer, or a blend of a propylene homopolymer and at least one propylene copolymer. When blends of homopolymers and copolymers are used in the film, the blends may comprise from about 5% to about 95% of the homopolymer and correspondingly from about 95% to about 5% by weight of the copolymer. The propylene homopolymers which may be utilized either alone or in combination with a propylene copolymer as described herein, include a variety of propylene homopolymers such as those having melt flow rates (MFR) from about 1 to about 20 as determined by ASTM Test D1238, condition L. Propylene homopolymers having MFRs of at least about 4 (preferably at least about 8) are particularly useful and provide films having improved die-cuttability. Useful propylene homopolymers also may be characterized as having densities in the range of about 0.88 to about 0.92 g/cm³.

A number of useful propylene homopolymers are available commercially from a variety of sources. Some of the useful homopolymers are listed and described in the following Table II. TABLE II Commercial Propylene Homopolymers Commercial Melt Flow Designation Company g/10 min Density (g/cm³) WRD5-1057 Union Carbide 12.0 0.90 DX5E66 Union Carbide 8.8 0.90 5A97 Union Carbide 3.9 0.90 5E98 Union Carbide 3.2 0.90 Z9470 Fina 5.0 0.89 Z9470HB Fina 5.0 0.89 Z9550 Fina 10.0 0.89 6671XBB Fina 11.0 0.89 3576X Fina 9.0 0.89 3272 Fina 1.8 0.89 SF6100 Montell 11.0 0.90

The propylene copolymers which may be utilized generally comprise copolymers of propylene and up to about 40% by weight of at least one alpha-olefin selected from ethylene and alpha-olefins containing from 4 to about 8 carbon atoms. Examples of useful alpha-olefins include ethylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-heptene, and 1-octene. More often, the copolymers of propylene which are utilized in the present invention comprise copolymers of propylene with ethylene, 1-butene or 1-octene. The propylene alpha-olefin copolymers useful in the present invention include random as well as block copolymers although the random copolymers generally are preferred. Blends of the copolymers as well as blends of the copolymers with propylene homopolymers can be utilized as the composition for the base layer. In one preferred embodiment, the propylene copolymers are propylene-ethylene copolymers with ethylenic contents of from about 0.2% to about 10% by weight. Preferably, the ethylene content is from about 3% to about 10% by weight and more preferably from about 3% to about 6% by weight. With regard to the propylene-1-butene copolymers, 1-butene contents of up to about 15% by weight are useful. In one embodiment, the 1-butene content generally may range from about 3% by weight up to about 15% by weight, and in other embodiments, the range may be from about 5% to about 15% by weight. Propylene-1-octene copolymers useful in the present invention may contain up to about 40% by weight of 1-octene. More often, the propylene-1-octene copolymers will contain up to about 20% by weight of 1-octene.

The propylene copolymers useful in the present invention may be prepared by techniques well known to those skilled in the art, and many such copolymers are available commercially. For example, the copolymers useful in the present invention may be obtained by copolymerization of propylene with an alpha-olefin such as ethylene or 1-butene using single-site metallocene catalysts. A list of some useful commercially available propylene copolymers is found in the following Table III. The propylene copolymers useful in the invention have an MFR of from about 1 to about 20, preferably from about 1 to about 12. TABLE III Commercial Propylene Copolymers Melt Flow Commercial % % 1- Rate (g/10 Density Name Source Ethylene Butene mins) (g/cm³) DS4D05 Union Carbide — 14 6.5 0.890 DS6D20 Union Carbide 3.2 — 1.9 0.890 DS6D81 Union Carbide 5.5 — 5.0 0.900 SRD4-127 Union Carbide —  8 8.0 NA SRD4-104 Union Carbide — 11 5.0 NA SRD4-105 Union Carbide — 14 5.0 NA

The monolayer films of the invention which are described above also are characterized as being free of copolymers of ethylene monomer with an ethylenically unsaturated carboxylic acid or ester comonomer. A film is considered to be free of such copolymers when there is less than about 0.1% by weight of such copolymers in the film. Specific examples of copolymers which are excluded from the films of this embodiment of the invention are the ethylene-vinyl acetate (EVA), ethylene methyl acrylate (EMA) and ethylene n-butyl acrylate (EnBA) copolymers.

Although the films of the invention may contain other polymers and copolymers, the presence of incompatible polymers and copolymers should be minimized or essentially avoided when a clear film (low haze) is desired. The amount of incompatible polymer which can be included depends on the particular polymer (e.g., degree of incompatibility) and the degree of haze that can be tolerated.

Various nucleating agents and particulate fillers can be incorporated into the monolayer films of the present invention. The amount of nucleating agent added should be an amount sufficient to provide the desired modification of the crystal structure while not having an adverse effect on the desired properties of the films. It is generally desired to utilize a nucleating agent to modify the crystal structure and provide a large number of considerably smaller crystals or spherulites to improve the transparency (clarity), stiffness, and the die-cuttability of the film. Obviously, the amount of nucleating agent added to the film formulation should not have a deleterious effect on the clarity of the film. Nucleating agents which have been used heretofore for polymer films include mineral nucleating agents and organic nucleating agents. Examples of mineral nucleating agents include carbon black, silica, kaolin and talc. Among the organic nucleating agents which have been suggested as useful in polyolefin films include salts of aliphatic mono-basic or di-basic acids or arylalkyl acids such as sodium succinate, sodium glutarate, sodium caproate, sodium 4-methylvalerate, aluminum phenyl acetate, and sodium cinnamate. Alkali metal and aluminum salts of aromatic and alicyclic carboxylic acids such as aluminum benzoate, sodium or potassium benzoate, sodium beta-naphtholate, lithium benzoate and aluminum tertiary-butyl benzoate also are useful organic nucleating agents. Substituted sorbitol derivatives such as bis (benzylidene) and bis (alkylbenzilidine) sorbitols wherein the alkyl groups contain from about 2 to about 18 carbon atoms are useful nucleating agents. More particularly, sorbitol derivatives such as 1,3,2,4-dibenzylidene sorbitol, 1,3,2,4-di-para-methylbenzylidene sorbitol, and 1,3,2,4-di-para-methylbenzylidene sorbitol are effective nucleating agents for polypropylenes. Useful nucleating agents are commercially available from a number of sources. Millad 8C-41-10 is a concentrate of 10% Millad 3988 (a sorbitol nucleating agent) and 90% polypropylene and is available from Milliken Chemical Co.

When a nucleating agent is incorporated into the film, the amounts of nucleating agent incorporated into the film formulations of the present invention are generally quite small and range from about 100 to about 2000 or 4000 ppm of the film. Preferably the amount of nucleating agent should not exceed about 2000 ppm, and in one embodiment, a concentration of about 300 to 500 ppm appears optimum.

The film may contain other additives and particulate fillers to modify the properties of the film. For example, colorants may be included in the film such as TiO₂, CaCO₃, etc. The presence of small amounts of TiO₂, for example, results in a white facestock. Antiblock agents also can be included in the base layer. AB-5 is an antiblock concentrate available from A. Schulman Inc., 3550 West Market Street, Akron, Ohio 44333, which comprises 5% solid synthetic amorphous silica in 95% low density polyethylene. ABPP05SC is an antiblock concentrate from Schulman containing 5% of the synthetic amorphous silica in a propylene copolymer. The amount of antiblock agent (silica) present in the base layer may range from about 500 to about 5000 ppm, with amounts of about 1000 ppm being preferred.

In some embodiments, particularly where it is desired that the film be clear, the film is free of inert particulate filler material although very small amounts of particulate filler material may be present in the film due to impurities etc. The term “free of” is intended to mean that the film contains less than about 0.1% by weight of particulate filler material. Films which are free of particulate filler are particularly useful when it is desired to prepare a film which is clear which may be characterized as having low haze, for example, less than 10%, or less than 6% haze, or in some instances less than about 2%. Haze or clarity is determined using a BYK-Gardner haze-gloss meter as known in the art. It has been observed that the biaxially stretch-oriented films of this invention which are free of filler particles exhibit improved clarity, and in some instances, the films are crystal clear. As noted above, incompatible polymers and copolymers are absent or present in minor amounts when clear films are desired.

The monolayer films of the present invention can be formed by a variety of techniques known to those skilled in the art including blown or cast extrusion, extrusion coating or by a combination of these techniques. The films of the present invention, as noted above, are biaxially stretch-oriented. Simultaneous biaxial orientation or sequential biaxial orientation may be utilized in preparing the films of the present invention. One preferred process is to produce the monolayer films by simultaneous biaxial orientation processes.

Although it is possible to prepare the desired die-cuttable, biaxially stretch-oriented monolayer films of the present invention by stretching the film in the machine direction (MD) in an amount which is equal to or greater than the stretching in the cross direction (CD), in one embodiment, it is preferred that the stretch orientation in the MD be greater than the orientation in the CD by at least about 10%, or even by 20%. The orientation in the MD may be at a stretch ratio of from about 3:1 to about 10:1 or higher although more often the stretch ratio in the MD is from about 5:1 to about 10:1. In other embodiments, the stretch ratio in the MD may range of from about 9:1 to about 10:1 or higher. As mentioned above, the stretch ratio in the CD often is less than the stretch orientation in the MD. Thus, stretch ratios in the CD may be from greater than 1:1 to about 5:1, or from greater than 1:1 to about 3:1 or greater than 1:1 to about 2:1. In a particular example of this latter embodiment, a monolayer film of a polyolefin stretch-oriented in the MD at a ratio of 9:1 to 10:1 is stretch oriented in the CD at a ratio of from greater than 1:1 to about 2:1 or 3:1 or 4:1. The polyolefins which may be utilized in this embodiment include polyethylenes, polypropylenes, copolymers of propylene and up to about 40% by weight of at least one alpha-olefin selected from ethylene and alpha-olefins containing from 4 to about 8 carbon atoms as described above, and mixtures thereof. Thus, in this particular embodiment, the polyolefins include low density polyethylene, medium density polyethylene and high density polyethylene, although the low and medium density polyethylenes are more often utilized. The high density polyethylenes are those having a density of greater than about 0.940 to about 0.965 g/cm³.

The monolayer films of the invention are biaxially oriented by hot stretching the films at a temperature equal to or above the softening temperature of the film. The temperatures utilized in the hot-stretching step will depend, among other things, on the film composition and whether any nucleating agents are present. When sequential orientation is utilized, the temperature for the MD stretching may not be the same as the temperature for the CD stretching. Generally, the MD orientation is conducted at a lower temperature than the CD orientation. For example, for a propylene homopolymer, the temperature for the MD orientation may be around 140° C. and the temperature for the CD orientation around 180° C.

In one embodiment of the present invention, the monolayer films which have been stretch oriented to the desired stretch ratio while in a heated condition are then passed over annealing rolls where the stretched films are annealed or heat-set. After the heat-setting or annealing operation, the film is then passed over a chill roll to complete the hot-stretch and heat-set operation. In another embodiment, the hot-stretched film is relaxed in both the MD and CD by from about 5 to about 25%, and more often from about 10 to about 20% prior to being subjected to the annealing or heat setting step. The temperature used in the hot-stretching step and the temperature utilized in the heat setting step depends on the particular polymer utilized to form the monolayer film, and these temperatures may range from about 110° C. to about 180° C. The temperatures utilized for the hot-stretching and the heat setting steps may be the same although in some instances, the temperature of the heat setting step is somewhat higher than the temperature utilized for the hot-stretching step. Thus, the heat setting step may be conducted at temperatures of up to about 180° C. When the hot stretched films of the present invention are subjected to a heat setting or annealing step, the film generally is heat set or annealed from about 5 to about 25 seconds, and more often, from about 10 to about 20 seconds. The stretch-oriented monolayer films of the present invention which are also heat-set or annealed are essentially devoid of “memory” of a pre-existing configuration to which a film tends to return under the influence of heat. That is, the heat-set and annealed films of the present invention do not have a tendency to shrink or distort when subsequently subjected to an elevated temperature.

The thickness of the monolayer films described above may range from about 0.5 mils (12.5 microns) to about 6 mils (150 microns) depending upon the anticipated utility of the film. More often, however, the biaxially stretch-oriented monolayer films of this invention have a thickness of from about 1 mil to about 3.5 or 4 mils. In one embodiment, the film thickness will range from about 2 to about 2.5 mils.

The biaxially stretch-oriented monolayer films of the present invention which have been described above exhibit stiffness characteristics which enable the films to be utilized in applications such as die-cuttable labelstock. Thus, the Gurley stiffness of the biaxially stretch-oriented monolayer films of the present invention may range from about 3 to about 50, more often from about 5 or 10 up to about 50 in the machine direction. The Gurley stiffness of the monolayer films of the invention in the cross direction will generally be less than the Gurley stiffness in the machine direction. The Gurley stiffness of the monolayer films of the present invention is measured in accordance with the TAPPI Gurley Stiffness Test T543pm.

As mentioned above, the films of the present invention also may comprise die-cuttable, stretch-oriented multilayer films which comprise

-   -   (A) a base layer having an upper surface and a lower surface,         and comprising polyethylene having a density of about 0.940         g/cm³ or less, a propylene homopolymer or copolymer, or mixtures         thereof wherein the base layer is free of copolymers of ethylene         with an ethylenically unsaturated carboxylic acid or ester, and     -   (B) a first skin layer of a thermoplastic polymer bonded to the         upper surface of the base layer, wherein the tensile modulus of         the multilayer film in the machine direction is greater than the         tensile modulus in the cross direction, and the tensile modulus         in the cross direction is about 150,000 psi or less.

Any of the monolayer films described above, prior to orientation, may be utilized as the base layer of the multilayer film. That is, the base layer of the multilayer films of the present invention may comprise any of the polyethylenes described above, any of the propylene homopolymers or copolymers described above, or mixtures thereof and wherein the base layer is free of copolymers of ethylene with an ethylenically unsaturated carboxylic acid or ester. The base layer also may contain any of the ingredients described above as being optional in the monolayer films such as fillers, colorants, nucleating agents, antiblock agents, etc. If a clear multilayer film is desired, the base layer will be free of inert particulate filler. If an opaque multilayer film is desired, the base layer may contain particulate fillers as described above.

The first skin layer may comprise any other variety of thermoplastic polymers. Examples of thermoplastic polymers and copolymers useful as the first skin layer of the multilayer film compositions of the present invention include polyolefins, polyamides, polystyrene, polystyrene-butadiene, polyester, polyester copolymer, polyurethane, polysulfone, polyvinylidene chloride, styrene-maleic anhydride copolymer, styrene acrylonitrile copolymer, ionomer based on sodium or zinc salts of ethylene methacrylic acid, polymethyl methacrylate, cellulosic, fluoroplastic, acrylic polymer and copolymer, polycarbonate, polyacrylonitrile, ethylene-vinyl acetate copolymer, and mixtures thereof. The composition of the first skin layer is a matter of choice depending on the properties desired for the first skin layer such as costs, weatherability, printability, etc.

The first skin layer may, and often does contain mixtures of polyolefins (e.g., polyethylene, propylene polymers and copolymers) and a copolymer of ethylene with an ethylenically unsaturated carboxylic acid or ester comonomer such as EVA. For example one useful skin composition comprises a 50:50 mixture of polypropylene and EVA.

The first skin layer may also contain other additives such as particulate fillers, antiblock agents, nucleating agents, etc., as described above. When a clear multilayer film is desired, the first skin layer (as well as the base layer), generally will be free of particulate filler material. When an opaque film is desired, the skin layer (and/or the base layer) will contain particulate filler material. Thus, it is possible to prepare the multilayer films of this invention ranging from opaque films to clear films, and the clear films may be characterized as having a haze of less than 10%, or less than 6%, or even less than about 2%.

In yet another embodiment of the present invention, the multilayer films described above comprising a base layer having an upper surface and a lower surface, and a first skin layer of a thermoplastic polymer bonded to the upper surface of the base layer, may also contain a second skin layer bonded to the lower surface of the base layer where the second skin layer may comprise any of the thermoplastic polymers described above as being useful in the first skin layer, and the composition of the second skin layer may be the same as or different from the composition of the first skin layer. Generally, the two skin layers are different since the properties desired for these layers are different. Printability, weatherability, etc. are desired for the first skin layer whereas other properties such as good bonding to an adhesive layer may be desired for the second skin layer.

The multilayer films of the present invention may be prepared by a variety of techniques known to those skilled in the art including blown or cast extrusion, or extrusion coating or by a combination of these techniques. U.S. Pat. No. 5,186,782 (Freedman), and U.S. Pat. No. 5,242,650 (Rackovan et al) and U.S. Pat. No. 5,435,963 (Rackovan et al) disclose useful procedures for preparing multilayer films, and these patents are hereby incorporated by reference. The multilayers can be formed by simultaneous extrusion from a suitable known type of coextrusion die, and the layers are adhered to each other in a permanently combined state to provide a unitary coextrudate. Alternatively, the base layer can be formed by extrusion of the base layer on a substrate followed by extrusion coating of the first skin layer (and optionally the second skin layer) onto the base layer thereby forming a two or three layer structure wherein the layers are adhered to each other in a permanently combined state. In another alternative embodiment, the two or three layers may be separately formed by extrusion and thereafter laminated together by the application of heat and pressure.

Generally, the base layer is relatively thick compared to the first skin layer and the second skin layer. In another, although generally not preferred embodiment, the first skin layer may be relatively thick compared to the base layer. Accordingly, thickness ratios for the three layered films may range from about 90:5:5 to 5:5:90. However, generally preferred thickness ratios for the three layered films (base: first skin:second skin) include 90:5:5, 80:10:10, 70:15:15, 85:5:10, and 80:5:15.

The multilayer films of the present invention, as noted above, are biaxially stretch-oriented. Simultaneous biaxial orientation or sequential biaxial orientation may be utilized in preparing the multilayer films of the present invention. Simultaneous biaxial orientation of the multilayer films of the present invention is a preferred process in one embodiment of the present invention.

Although in some instances, it is possible to prepare the desired die-cuttable, biaxially stretch-oriented multilayer films of the present invention by stretching the film in the machine direction (MD) in an amount which is equal to or greater than the stretching in the cross direction (CD), the stretch orientation in the MD more often will be greater than the orientation in the CD by at least about 10%, or even by 20%. The orientation in the MD may be at a stretch ratio of from about 3:1 to about 10:1 or higher although a preferred stretch ratio in the MD is from about 5:1 to about 10:1. In other embodiments, the stretch ratio in the MD is within the range of from about 9:1 to about 10:1 or higher. As mentioned above, the stretch ratio in the CD generally is less than the stretch orientation in the MD. Thus, stretch ratios in the CD are from greater than 1:1 to about 5:1, or from greater than 1:1 to about 3:1 or greater than 1:1 to about 2:1.

The thickness of the multilayer films described above will range from about 0.5 mils (12.5 microns) to about 6 mils (150 microns) depending upon the anticipated utility of the film. More often, however, the multilayer films of the present invention will have a thickness of about 1 to about 3.5 or 4 mils or from about 2 to about 3 mils. Such thicknesses are particularly useful for preparing labels to be applied to rigid and flexible substrates. As noted earlier, a particular feature of the multilayer film facestocks of the invention is that very thin films (i.e., 1 to 3 mils) can be prepared that are useful in forming labels.

The selection of a particular polymer for the second skin layer is dependent on the properties and characteristics which are to be added by the presence of the second skin layer. The polymer for the second skin layer should be compatible with the polymer of the base layer to provide sufficient adhesion to the base layer. For example, if the base layer contains a propylene polymer, a second skin layer comprising at least some propylene polymer will adhere to the base layer without an intermediate tie layer. It also has been discovered that the use of a composition in the second skin layer that is different from the composition of the first skin layer reduces the blocking tendency when the facestock is rolled on itself.

In one embodiment, it is preferred that the second skin layer comprise a polymer that is softer than the propylene polymer or copolymer, or blends of propylene polymers and copolymers used in the base layer, particularly when the second skin layer is joined with an adhesive to a release coated liner. In particular, it is preferred that the material of the second skin layer has a lower tensile modulus than the tensile modulus of the material comprising the base layer. The use of a lower tensile modulus second skin layer results in a facestock exhibiting improved die-cuttability when compared to a facestock wherein the material of the second skin layer has a higher tensile modulus than the material of the base layer.

The stiffness of the multilayer films of the present invention is important for proper dispensing of labels over a peel plate at higher line speeds. Biaxial orientation of the multilayer films increases the tensile modulus in the machine direction and cross direction. The increase in the machine direction contributes to dimensional stability and good print registration.

The stiffness of the oriented multilayer films in the machine direction generally should be at least about 2 or 3, and may be as high as 50 or 60 Gurley. More often the stiffness of the oriented multilayer films in the MD is in the range of from about 5 or 10 up to about 25 or 35 Gurley as measured in accordance with the TAPPI Gurley Stiffness Test T543pm. The Gurley stiffness in the CD generally is in the same ranges but the stiffness in the CD is less than the stiffness in the MD.

The biaxially stretch-oriented monolayer films and multilayer films of the present invention which have been described above are further characterized as having a tensile modulus in the cross direction of about 150,000 psi or less. The tensile modulus of the films can be determined in accordance with ASTM Test D882 entitled “Tensile Properties of Thin Plastic Sheeting”. In one embodiment of the invention, the tensile modulus of the films of the present invention in the cross direction is less than the tensile modulus of the films in the machine direction. Labels prepared from such films are observed to exhibit improved conformability. Thus, in one embodiment, the tensile modulus of the films of the present invention in the machine direction may be as high as 200,000 psi or even as high as 250,000 psi, and the tensile modulus in the cross direction is 150,000 psi or less. In other embodiments, the tensile modulus in the machine direction is 150,000 or less or even 125,000 or less, and the tensile modulus in the cross direction is less than 100,000 psi.

The following Examples identified in Table IV illustrate the monolayer films of the present invention. Unless otherwise indicated in the following Examples and elsewhere in the specification and claims, all parts and percentages are by weight, temperatures are in degrees centigrade, and pressures are at or near atmospheric pressure.

The films in the following Table IV are prepared by extruding the melted charges through an extrusion die and casting on cooling rolls. The extrudate is in the form of sheets which are cut to 10×10 cm² and subsequently biaxially hot-stretched on a laboratory film stretcher at the ratios specified in Table IV at a draw rate of 400%/second. The stretcher is a type KARO IV stretcher manufactured by Bruckner Maschinenbau. The oriented films are relaxed and annealed (heat set) as set forth in Table IV. Some of the properties of the monolayer films of Examples 1-11 are reported in Table V. TABLE IV Biaxially Stretch-Oriented Monolayer Films Film Stretch Ratio Orientation Anneal Thickness Example Composition MD CD Temp (° C.) Relaxation %¹ Period (sec.)² (Mils) 1 11G1 7:1 5:1 122 10 20 2.26 2 11G1 8:1 5:1 118 10 20 1.82 3 11G1 8:1 5:1 122 10 20 1.40 4 6D81 5:1 5:1 122 10 20 3.28 5 6D81 8:1 4:1 130 10 20 2.58 6 6D81 9:1 4:1 130 10 20 2.30 7 DS4DO5 8:1 4:1 130 10 20 2.46 8 DS4DO5 10:1  2.5:1   130 10 20 3.24 9 DS4DO5 10:1  4:1 130 10 20 2.16 10 5E98 + 2% NA³ 10:1  2.5:1   160 10 10 2.86 11 DS5E98 10:1  2.5:1   160 10 10 2.07 ¹Percent reduction in MD and CD stretch ratio ²Anneal temperature is same as orientation temperature ³Millad 8C41-10

TABLE V Properties of Biaxially Stretch-Oriented Monolayer Films 2% Secant Thickness Gurley Stiffness Modulus (psi) Haze Example (Mils) MD CD MD CD (%) 1 2.26 7.0 5.8 63,600 33,100 1.7 2 1.82 3.9 3.4 42,200 28,500 2.1 3 1.40 1.7 1.6 42,200 32,700 4.6 4 3.28 28.3 27.2 73,300 72,800 1.1 5 2.58 15.2 10.1 80,000 74,700 1.3 6 2.30 11.8 7.2 89,100 67,800 1.3 7 2.46 16.6 12.6 113,300 87,800 0.9 8 3.24 43.6 29.6 152,000 93,300 0.9 9 2.16 12.8 7.2 134,500 99,800 0.7 10 2.86 51.9 32.4 234,300 149,400 4.9 11 2.07 18.6 11.3 235,600 145,500 5.2

The following Examples 12-14 illustrate the multilayer films of the invention. The multilayer films are prepared by coextrusion as described above. The films are biaxially oriented at the ratios and at the temperatures shown in Table VI. The draw rate is 400%/second. Some of the properties of the films of Examples 12-14 are reported in Table VII. TABLE VI Biaxially Stretch-Oriented Multilayer Films Overall Base Skin Thickness Stretch Ratio Orientation Relaxation Anneal Period Example Layer Layer (Mils) MD CD Temp (° C.) (%)¹ (Sec)² 12 11G1 2027 2.14 7:1 5:1 118 10 20 13 11G1 2027 2.52 8:1 4:1 130 10 20 14 6D81 50%5E98 2.76 8:1 4:1 130 10 20 50% EVA* *Equistar UESP242F; EVA containing 18% VA ¹Percent reduction in MD and CD Stretch Ratio ²Anneal temperature is same as orientation temperature

TABLE VII Properties of Biaxially Stretch-Oriented Multilayer Films Overall 2% Secant Thickness Gurley Stiffness Modulus (psi) Example (Mils) MD CD MD CD Haze (%) 12 2.14 4.8 4.4 43,700 33,600 2.6 13 2.52 17.4 11.3 86,900 71,100 5.6 14 2.76 16.8 12.2 73,000 63,000 71.1

The die-cuttability of the biaxially oriented films of Examples 1-14 is evaluated by die-cutting shapes in the films and thereafter measuring the friction energy required to separate the matrix from the die-cut shape. A low friction energy value (e.g., about 150 g-cm or less) indicates the film exhibits good die-cuttability. Friction energy values of less than 120 and even less than 100 are particularly desirable. This test which is conducted as follows is described in more detail in U.S. Pat. No. 5,961,766 entitled “Method For Selecting A Substrate Intended For Use In A Cutting Operation”, which patent is hereby incorporated by reference.

A test sheet of each film having the dimensions of 7×10″ (17.8×25.4 cm) and a paper liner are advanced through a die-cutter where 10 shapes are cut in the film but not the liner. The die-cutter has a cylindrical profile. The die-cutting roll has a diameter of 3 inches (76.2 mm), with one cavity across and 10 cavities around. Each of the cavities are 6 inches (152.4 mm) long (or across), {fraction (15/16)} inch (22.25 mm) wide (or deep) and have rounded corners with diameters of {fraction (3/32)} inch (2.38 mm). The separation between adjacent cavities is {fraction (1/8)} inch (3.175 mm). The anvil roll has a diameter of 5 inches (127 mm). The gap between the anvil and the tip of the die is 2.2 mils (0.0559 mm). The die pressure is 300 psi (208500 kg/m²), and the speed of the die is 15 m/min.

The die-cut in each test sheet is deep enough to penetrate the film but not the liner. The shapes that are formed are rectangular and arranged side-by-side on the test sheet, one shape across and ten deep. The long dimension of each shape is parallel to the long dimension of the next adjacent shape. The shapes have the dimensions of ⅞×6″ (22.25 mm×152.4 mm) and are equidistant from each other. The gap between each shape is {fraction (1/8)} inch (3.175 mm). A matrix, which consists of the portion of the waste facestock around the shapes, is also formed during the die-cutting.

A test sample is formed by cutting the die-cut test sheet along the center line of the long dimension of one shape and then along the center line of the long dimension of the next adjacent shape. The cuts are parallel to each other. Each test sample consists of one-half of one shape, one-half of the next adjacent shape, the matrix around the shape portions.

The friction energy required to separate the matrix from the die-cut shapes of each sample is measured using a modified TA-XT2 Texture Analyzer provided by Stable Micro Systems, Unit 105, Blackdown Rural Industries, Haste Hill, Haslemere, Surrey GU 27 3AY, England. The TA-XT2 Texture Analyzer is a tensile testing device. It is modified as follows: the fixture on the top crosshead is removed and substituted by an upper L-shaped bracket; one arm of the upper L-shaped bracket is attached to the upper frame; the platform mounted on the base is removed and substituted by a lower L-shaped bracket. Each test sample is tested by attaching an edge of the matrix of the test sample to the upper L-shaped bracket, and attaching the edge of each shape portion adjacent to the attached matrix edge to the lower L-shaped bracket. The texture analyzer is activated and the matrix is separated from the shape portions at a rate of 5 mm/s.

The force used to separate the matrix and the displacement of this force along the length of the test sample during separating is plotted using software provided with the TA-XT2 Texture Analyzer. The area under the plot is also determined using software provided with the TA-XT2 Texture Analyzer. The area under the plot has the units of gram-seconds. The result is multiplied by the stripping speed (5 mm/s) and after making appropriate corrections for units (i.e., mm to cm), the friction energy results are provided in terms of gram-centimeters (g-cm). Higher friction energy numbers are associated with poorly cut facestocks or adhesive flowback. The test results for the films of Examples 1-14 are summarized in Table VIII. For each film, about seven test samples are tested and the averages for these test samples are given in Table VIII. TABLE VIII Friction Energy Test Results Film of Friction Energy Example (g-cm) 1 68 2 93 3 109 4 54 5 51 6 41 7 74 8 85 9 43 10 40 11 65 12 57 13 54 14 36

In another embodiment of the present invention, the biaxially oriented monolayer or multilayer films of the present invention may be utilized for preparing labelstock for adhesive labels. The labelstock comprises the monolayer film or the multilayer film described above, and an adhesive layer which is adhesively joined to one surface of the film.

In one embodiment, an adhesive containing labelstock used in adhesive labels comprises

-   -   (A) a die-cuttable, biaxially oriented multilayer film         comprising         -   (A-1) a base layer having an upper surface and a lower             surface, and comprising polyethylene having a density of             about 0.940 g/cm³ or less, a propylene polymer or copolymer,             or mixtures thereof wherein the base layer is free of             copolymers of ethylene with an ethylenically unsaturated             carboxylic acid or ester, and         -   (A-2) a first skin layer of a thermoplastic polymer bonded             to the upper surface of the base layer, wherein the tensile             modulus of the multilayer film in the machine direction is             greater than the tensile modulus in the cross direction, and             the tensile modulus of the multilayer film in the cross             direction is 150,000 psi or less, and     -   (B) an adhesive layer having an upper surface and a lower         surface wherein the upper surface of the adhesive layer is         adhesively joined to the lower surface of the base layer.

The multilayer film useful in such labelstock is described in detail above. The adhesive layer in this embodiment is adhesively joined to the lower surface of the base layer. Additionally, the biaxially oriented multilayer film (A) may comprise (A-3) a second skin layer bonded to the lower surface of the base layer, and thus, the second skin layer is between the base layer and the adhesive layer. The second skin layers as described above can be utilized.

The adhesive layer may be directly coated on the lower surface of the base layer, or to the second skin layer when present, or the adhesive may be transferred from a liner with which the multilayer film is combined. Typically, the adhesive layer has a thickness in the range of from about 0.1 to about 2 mils (2.5 to 50 microns). Adhesives suitable for use in labelstocks of the present invention are commonly available in the art. Generally, these adhesives include pressure-sensitive adhesives, heat-activated adhesives, hot melt adhesives, and the like. Pressure-sensitive adhesives are particularly preferred. These include acrylic adhesives as well as other elastomers such as natural rubber or synthetic rubbers containing polymers or copolymers of styrene, butadiene, acrylonitrile, isoprene and isobutylene. Pressure-sensitive adhesives are well known in the art and any of the known adhesives can be used with the facestocks of the present invention. In one preferred embodiment, the pressure-sensitive adhesives are based on copolymers of acrylic acid esters, such as, for example, 2-ethyl hexyl acrylate, with polar comonomers such as acrylic acid.

In the manufacture of labelstock from the above-described monolayer and multilayer films in accordance with the invention, liner or carrier stock may be provided. The liner or carrier stock may comprise a multilayer liner made for example as disclosed in U.S. Pat. No. 4,713,273, the disclosure which is incorporated herein by reference, or may be a conventional liner or carrier consisting of a single paper of film layer which may be supplied in roll form. If it has not been previously provided with a release coating and does not itself include components to inherently generate a release surface at its adhesive-contacting face, the liner or carrier may be coated with a release coating (e.g., a silicone). If a release coating is applied, it is dried or cured following application by any suitable means.

The release face of the release liner or carrier may be coated with a layer of pressure-sensitive adhesive for subsequent transfer of the adhesive to the labelstock with which the liner or carrier is employed. When the labelstock is combined with the liner or carrier, the adhesive is joined to the biaxially oriented film. Later, the liner or carrier is removed to expose the adhesive, and the adhesive remains permanently joined to the biaxially oriented film.

In some applications, the adhesive layer may be a heat-activated adhesive or a hot-melt adhesive such as used in in-mold label applications, as distinguished from a pressure-sensitive adhesive. If the adhesive is a heat-activated adhesive or a hot-melt adhesive, there may be no need for the provision of a release liner for inherent releasability such as is required when using a pressure-sensitive adhesive.

The manufacture of pressure-sensitive adhesive labelstock from the above-described biaxially oriented films in accordance with the invention is illustrated as follows. The liner or carrier stock may comprise a multilayer liner or a conventional liner or carrier consisting of a single paper or film layer having a release coating which may be supplied in roll form. The release face of the release liner or carrier may be coated with a layer of pressure-sensitive adhesive for subsequent transfer of the adhesive to the oriented film with which the liner or carrier is employed. When the film is combined with the liner or carrier, the adhesive is joined to the film. Later, the liner or carrier is removed to expose the adhesive, which now remains permanently joined to the biaxially oriented film.

The biaxially oriented film may be printed prior to being die-cut into individual labels. The printing step may occur before or after the combining of liner and oriented film, but will precede the die-cutting of the labelstock into individual labels. The film must remain in accurate register between printing steps (for example, between successive impressions in different colors) in order that image or text be of high quality, and between printing and subsequent die-cutting in order that image or text be located properly on the labels. The film is under tension during printing, and may be subjected to some increase in temperature, as for example when UV inks are cured, and the film must maintain dimensional stability in the machine-direction.

As noted earlier, the biaxially stretch-oriented films of this invention are die-cuttable, and the labelstock on a liner may be die-cut into a series of spaced pressure-sensitive labels carried by the release liner or carrier. This step may be performed by cutting dies (e.g., rotary cutting dies) in a well-known manner and involves the subsequent stripping of the ladder-shaped matrix of waste or trim surrounding the formed labels when they are die-cut (the “rungs” of the ladder representing the spacing between successive labels). The labels then remain on the liner in spaced relation with each other. One failure mode in this operation involves poorly die-cut labels remaining with the matrix as it is stripped. In this mode, as release levels decrease, poor die-cutting is more likely to cause labels to stay attached to the matrix material and be removed from the liner during matrix stripping along with the matrix. Another failure mode occurs when the die-cut goes through the adhesive and part of the liner leaving an impression in the liner. Another failure mode results when the films being die-cut are of insufficient strength. As the strength of the matrix material decreases, the matrix tends to tear as the matrix around the die-cut labels is pulled from the liner. The films of the present invention have sufficient strength to avoid or reduce breakage of the matrix on stripping.

The die-cut labels on the liner or carrier can be dispensed and applied to various substrates by techniques known to those skilled in the art. For example, the labels can be dispensed and applied to passing workpieces by use of a peel-back edge to dispense the labels by progressively removing the liner or carrier from them to thereby expose the adhesive side of the labels and project the labels into contact with passing workpieces. In the context of the present invention, the workpieces may constitute substrates such as glass bottles or other rigid articles tending to have irregularities in the surface and therefore requiring labels that are flexible and that closely adhere (conform) to the surface without bridging local surface depressions. The substrates also may be flexible plastic containers.

While the invention has been explained in relation to its preferred embodiments, it is to be understood that various modifications thereof will become apparent to those skilled in the art upon reading the specification. Therefore, it is to be understood that the invention disclosed herein is intended to cover such modifications as fall within the scope of the appended claims. 

1. A die-cuttable, stretch-oriented multilayer film comprising (A) a base layer having an upper surface and a lower surface, and comprising polyethylene having a density of about 0.940 g/cm³ or less, a propylene homopolymer or copolymer, or mixtures thereof wherein the base layer is free of copolymers of ethylene with an ethylenically unsaturated carboxylic acid or ester, and (B) a first skin layer of a thermoplastic polymer bonded to the upper surface of the base layer, wherein the tensile modulus of the multilayer film in the machine direction is greater than the tensile modulus in the cross direction, and the tensile modulus in the cross direction is about 150,000 psi or less.
 2. The film of claim 1 wherein the base layer is free of inert particulate filler.
 3. The multilayer film of claim 1 wherein the base layer comprises a propylene copolymer.
 4. The multilayer film of claim 1 wherein the base layer comprises a propylene copolymer which is a copolymer of propylene and up to about 40% by weight of at least one α-olefin selected from ethylene and α-olefins containing from 4 to about 8 carbon atoms.
 5. The film of claim 4 wherein the α-olefin is ethylene or 1-butene.
 6. The multilayer film of claim 1 wherein the base layer comprises polyethylene having a density of from about 0.890 to about 0.925 g/cm³.
 7. The multilayer film of claim 1 wherein the first skin layer (B) contains inert particulate filler.
 8. The multilayer film of claim 1 wherein the first skin layer (B) is free of inert particulate filler.
 9. The multilayer film of claim 1 having a haze of less than 10%.
 10. The multilayer film of claim 1 having a haze of less than 6%.
 11. The multilayer film of claim 1 wherein the first skin layer comprises at least one polyolefin, polyamide, polystyrene, polystyrene-butadiene, polyester, polyester copolymer, polyurethane, polysulfone, polyvinylidene chloride, styrene-maleic anhydride copolymer, styrene acrylonitrile copolymer, ionomer based on sodium or zinc salts of ethylene methacrylic acid, polymethyl methacrylate, cellulosic, fluoroplastic, acrylic polymer and copolymer, polycarbonate, polyacrylonitrile, ethylene-vinyl acetate copolymer, and mixtures thereof.
 12. The multilayer film of claim 1 wherein the base layer and the first skin layer are formed by coextrusion.
 13. The multilayer film of claim 1 wherein the stretch-orientation in the machine direction is greater than the orientation in the cross direction by at least 10%.
 14. The multilayer film of claim 1 which has been oriented in the machine direction at a stretch ratio of from about 5:1 to about 10:1.
 15. The multilayer film of claim 1 wherein the base layer or first skin layer, or both, also contain a nucleating agent.
 16. The multilayer film of claim 1 containing a second skin layer bonded to the lower surface of the base layer.
 17. The multilayer film of claim 16 wherein the composition of the second skin layer is different from the composition of the first skin layer.
 18. The multilayer film of claim 1 having a Gurley stiffness in the machine direction of from about 10 to about
 50. 19. The multilayer film of claim 1 having an overall thickness of from about 2 to about 3 mils.
 20. The multilayer film of claim 1 wherein the film has been biaxially stretch-oriented and heat set.
 21. The multilayer film of claim 1 wherein the multilayer film has been stretch oriented in the machine direction at a ratio of from about 9:1 to about 10:1, and in the cross direction at a ratio of from greater than 1:1 to about 3:1.
 22. The multilayer film of claim 1 having a friction energy of less than
 120. 23. The multilayer film of claim 1 having a friction energy of less than
 80. 24. The multilayer film of claim 1 having an overall thickness of from 1 to about 3.5 mils.
 25. The multilayer film of claim 1 wherein the film has been stretched in the cross direction at a ratio of from greater than 1:1 up to about 5:1.
 26. The film of claim 1 wherein the biaxially oriented film is prepared by a simultaneous biaxial orientation process.
 27. A die-cuttable, biaxially stretch-oriented multilayer film comprising (A) a base layer having an upper surface and a lower surface, and comprising polyethylene having a density of from about 0.940 g/cm³ or less, a propylene polymer or copolymer, or mixtures thereof wherein the base layer is free of copolymers of ethylene with an ethylenically unsaturated carboxylic acid or ester, and (B) a first skin layer of a thermoplastic polymer bonded to the upper surface of the base layer, wherein the stretch-orientation of the multilayer film in the machine direction is greater than the stretch-orientation in the cross direction by at least 10%, and the tensile modulus of the multilayer film in the cross direction is 150,000 psi or less.
 28. The film of claim 27 wherein the stretch-orientation in the machine direction is greater than the stretch-orientation in the cross direction by at least about 20%.
 29. The film of claim 27 wherein the film has been stretched in the machine direction at a ratio of from about 5:1 to about 10:1.
 30. The film of claim 27 wherein the base layer comprises a copolymer of propylene and up to about 40% by weight of at least one α-olefin selected from ethylene and α-olefins containing from 4 to about 8 carbon atoms.
 31. The film of claim 27 wherein the base layer comprises a polyethylene having a density of from about 0.890 to about 0.925 g/cm³.
 32. The multilayer film of claim 27 having an overall thickness of from 1 to about 3.5 mils.
 33. The multilayer film of claim 27 wherein the film has been stretched in the cross direction at a ratio of from greater than 1:1 up to about 5:1.
 34. The multilayer film of claim 27 having a haze of less than 10%.
 35. The multilayer film of claim 27 wherein the biaxially oriented film is prepared by a simultaneous biaxial orientation process.
 36. A die-cuttable, stretch-oriented multilayer film having an overall thickness of from about 1 mil to about 3.5 mils and comprising (A) a base layer having an upper surface and a lower surface, and comprising polyethylene having a density of about 0.940 g/cm³ or less, a propylene homopolymer or copolymer, or mixtures thereof wherein the base layer is free of copolymers of ethylene with an ethylenically unsaturated carboxylic acid or ester, and (B) a first skin layer of a thermoplastic polymer bonded to the upper surface of the base layer, wherein the tensile modulus of the multilayer film in the machine direction is greater than the tensile modulus in the cross direction, the tensile modulus in the cross direction is about 150,000 psi or less, the multilayer film has been oriented in the machine direction at a stretch ratio of from about 5:1 to about 10:1 and in cross-direction at a stretch ratio of from greater than 1:1 up to about 5:1 provided the stretch ratio in the cross direction is less than the stretch ratio in the machine direction, and the film is free of copolymers of ethylene with an ethylenically unsaturated carboxylic acid or ester.
 37. A die-cuttable, biaxially stretch-oriented multilayer film having an overall thickness of from about 1 mil to about 3.5 mils and comprising (A) a base layer having an upper surface and a lower surface, and comprising polyethylene having a density of from about 0.940 g/cm³ or less, a propylene polymer or copolymer, or mixtures thereof wherein the base layer is free of copolymers of ethylene with an ethylenically unsaturated carboxylic acid or ester, and (B) a first skin layer of a thermoplastic polymer bonded to the upper surface of the base layer, wherein the stretch-orientation of the multilayer film in the machine direction is greater than the stretch-orientation in the cross direction by at least 10%, the tensile modulus of the multilayer film in the cross direction is 150,000 psi or less, the multilayer film has been oriented in the machine direction at a stretch ratio of from about 5:1 to about 10:1 and in cross-direction at a stretch ratio of from greater than 1:1 up to about 5:1, and the film is free of copolymers of ethylene with an ethylenically unsaturated carboxylic acid or ester.
 38. A die-cuttable, biaxially stretch oriented monolayer film comprising at least one polyolefin wherein the film has been stretch oriented in the machine direction at a stretch ratio of about 9:1 to about 10:1, and in the cross direction at a stretch ratio of from greater than 1:1 to about 3:1.
 39. The film of claim 38 wherein the stretch ratio in the cross direction is less than 2:1.
 40. The film of claim 38 wherein the film comprises, polyethylene, a propylene polymer or copolymer, or mixtures thereof.
 41. The film of claim 38 wherein the film comprises a copolymer or propylene and ethylene or at least one a-olefin containing from 4 to about 8 carbon atoms.
 42. A die-cuttable, stretch oriented multilayer film comprising (A) a base layer having an upper surface and a lower surface, and comprising at least one polyolefin, (B) a first skin layer of thermoplastic polymers bonded to the upper surface of the base layer wherein the multilayer film has been stretch oriented in the machine direction at a stretch ratio of from 9:1 to about 10:1, and in the cross direction at a stretch ratio of greater than 1:1 to about 3:1.
 43. The multilayer film of claim 42 wherein the multilayer film has been stretch oriented in the cross direction at a ratio of less than 2:1. 